WH60A低合金高强度钢板的拉伸性能/冶炼方法/
2 化学成分
|
化 学 成 分，% |
|||||
|
C |
Si |
Mn |
P |
S |
Ceq |
|
≤0.18 |
≤0.55 |
≤1.98 |
≤0.025 |
≤0.020 |
≤0.50 |
2) 碳当量(Ceq,%)计算公式如: Ceq(%)=C+Mn/6+(Cr+Mo+V)/5+(Ni+Cu)/15
3 常用规格尺寸
|
材质- |
厚度mm |
宽度mm |
长度mm |
|
WH60A |
8-12 |
2000-2500 |
8000-12000 |
|
WH60A |
12-16 |
2000-2500 |
8000-12000 |
|
WH60A |
16-50 |
2000-2500 |
8000-12000 |
|
WH60A |
50-80 |
2000-2500 |
8000-12000 |
|
WH60A |
80-100 |
2000-2500 |
8000-12000 |
|
WH60A |
100-120 |
2000-2500 |
8000-12000 |
|
WH60A |
120-150 |
2000-2500 |
8000-12000 |
|
WH60A |
150-200 |
2000-2500 |
8000-12000 |
|
材质 |
厚度 |
宽度 |
长度 |
|
WH60A |
8 |
2200 |
12000 |
|
WH60A |
10 |
2200 |
10000 |
|
WH60A |
10 | 2480 |
10000 |
|
WH60A |
12 |
2500 |
12000 |
|
WH60A |
16 |
2500 |
13000 |
|
WH60A |
20 |
2500 |
12800 |
|
WH60A |
25 |
2350 |
12000 |
|
WH60A |
30 |
2200 |
12000 |
|
WH60A |
35 |
2200 |
10000 |
|
WH60A |
40 |
2500 |
11000 |
|
WH60A |
45 |
3040 |
12950 |
|
WH60A |
50 |
2450 |
11100 |
|
WH60A |
60 |
2200 |
11800 |
|
WH60A |
70 |
2200 |
12000 |
|
WH60A |
80 |
2200 |
12000 |
|
WH60A |
90 |
2200 |
10000 |
|
WH60A |
100 |
2200 |
10000 |
|
WH60A |
120 |
2300 |
12300 |
|
WH60A |
150 |
2300 |
10500 |
|
WH60A |
150 |
2300 |
8350 |
4 力学性能
|
牌号 |
规格 |
拉伸性能 |
AKv,J,纵向 |
延伸率 |
180°弯曲试验 d=弯心直径 a=试样厚度 |
|
WH60A |
≤16 |
≥460 |
560- 780 |
≥ 17 |
d=2a |
|
>16-35 |
≥440 |
d=3a | |||
|
>35-50 |
≥420 |
||||
|
>50-100 |
≥400 |
7 各项检验的检验项目、取样数量、取样方法和实验方法
|
序号 |
检验项目 |
取样数量（个） |
取样方法 |
试验方法 |
|
1 |
化学分析 |
1（每炉罐号） |
GB/T222 |
GB/T223 |
|
2 |
拉伸 |
1 |
GB/T2975 |
GB/T228 |
|
3 |
夏比冲击 (V型缺口) |
3 |
GB/T2975 |
GB/T229 |
|
4 |
弯曲 |
1 |
GB/T2975 |
GB/T232 |
8 现货较少，期货定轧，切割加工下料